玻璃纤维增强材料30%,抗冻, 抗溶剂性, 耐疲劳性能, 流动性高, 汽车的发动机罩下的零件

 

Vydyne® R530H NAT

聚酰胺66

Ascend Performance Materials Operations LLC

Technical Data

 

产品说明

 

Vydyne R530H NAT is general-purpose, heat-stabilized, hydrolysis-resistant, 30% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is also lubricated for improved machine feed and flow.

 

Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.

 

Vydyne R530H NAT is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R530H NAT has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions.

 

Typical Applications/End Uses:

Vydyne R530H NAT has been used for several under-the-hood automotive applications. The hydrolysis-resistant properties make it an excellent candidate for radiator end tank and heater core applications.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet

UL 黄卡 2 •  E70062-249083

搜索 UL 黄卡 •  Ascend Performance Materials Operations LLC

•  Vydyne®

供货地区 • 北美洲 • 欧洲 • 亚太地区

填料/增强材料 • 玻璃纤维增强材料, 30% 填料按重量

添加剂 • 热稳定剂 • 润滑剂

• 抗冻 • 耐化学性良好 • 耐水解性

特性 • 抗溶剂性 • 耐疲劳性能 • 热稳定性

• 良好的流动性 • 耐汽油性 • 润滑

用途 • 汽车的发动机罩下的零件

机构评级 • ASTM D 4066 PA0121G30 • ASTM D 6779 PA0121G30

UL文件号 • E70062

外观 • 自然色

形式 • 粒子

加工方法 • 注射成型

物理性能 干燥 调节后的 单位制 测试方法

密度 1.37 -- g/cm³ ISO 1183

收缩率 ISO 294-4

垂直流动方向 : 23°C, 2.00 mm 0.90 -- %

流动方向 : 23°C, 2.00 mm 0.40 -- %

吸水率 ISO 62

23°C, 24 hr 0.90 -- %

平衡, 50% RH 1.9 -- %

机械性能 干燥 调节后的 单位制 测试方法

拉伸模量 (23°C) 10000 7400 MPa ISO 527-2

拉伸应力 (断裂, 23°C) 195 135 MPa ISO 527-2

拉伸应变 (断裂, 23°C) 3.0 5.0 % ISO 527-2

弯曲模量 (23°C) 9600 6000 MPa ISO 178

弯曲应力 (23°C) 270 190 MPa ISO 178

Poisson's Ratio (23°C) 0.40 -- ISO 527

 

Vydyne® R530H NAT

聚酰胺66

Ascend Performance Materials Operations LLC

冲击性能 干燥 调节后的 单位制 测试方法

简支梁缺口冲击强度 ISO 179

-30°C 10 11 kJ/m²

23°C 11 13 kJ/m²

简支梁无缺口冲击强度 ISO 179

-30°C 65 80 kJ/m²

23°C 75 85 kJ/m²

悬壁梁缺口冲击强度 ISO 180

-30°C 10 11 kJ/m²

23°C 12 13 kJ/m²

热性能 干燥 调节后的 单位制 测试方法

热变形温度

0.45 MPa, 未退火 260 -- °C ISO 75-2/B

1.8 MPa, 未退火 250 -- °C ISO 75-2/A

熔融温度 260 -- °C ISO 11357-3

线形热膨胀系数 ISO 11359-2

流动 : 23 到 55°C, 2.00 mm 2.2E-5 -- cm/cm/°C

横向 : 23 到 55°C, 2.00 mm 1.1E-4 -- cm/cm/°C

RTI Elec UL 746

0.750 mm 140 -- °C

1.50 mm 140 -- °C

3.00 mm 140 -- °C

RTI Imp UL 746

0.750 mm 120 -- °C

1.50 mm 120 -- °C

3.00 mm 120 -- °C

RTI UL 746

0.750 mm 125 -- °C

1.50 mm 140 -- °C

3.00 mm 140 -- °C

电气性能 干燥 调节后的 单位制 测试方法

体积电阻率 (3.00 mm) 1.0E+13 -- ohm•cm IEC 60093

介电强度 (1.00 mm) 20 -- kV/mm IEC 60243

耐电弧性 (3.00 mm) PLC 6 -- ASTM D495

漏电起痕指数 (3.00 mm) 250 到 399 -- V IEC 60112

高电弧燃烧指数(HAI) UL 746

0.750 mm PLC 0 --

1.50 mm PLC 0 --

3.00 mm PLC 0 --

高电压电弧起痕速率 (HVTR) PLC 1 -- UL 746

热丝引燃 (HWI) UL 746

0.750 mm PLC 4 --

1.50 mm PLC 3 --

3.00 mm PLC 4 --

可燃性 干燥 调节后的 单位制 测试方法

UL 阻燃等级 UL 94

0.750 mm HB --

1.50 mm HB --

3.00 mm HB --

灼热丝易燃指数 IEC 60695-2-12

0.750 mm 675 -- °C

1.50 mm 675 -- °C

3.00 mm 675 -- °C

 

Vydyne® R530H NAT

聚酰胺66

Ascend Performance Materials Operations LLC

可燃性 干燥 调节后的 单位制   测试方法

热灯丝点火温度 IEC 60695-2-13

0.750 mm 700 -- °C

1.50 mm 700 -- °C

3.00 mm 700 -- °C

注射 干燥单位制

干燥温度 80.0°C

干燥时间 4.0hr

建议的最大回制料比例 25%

料筒后部温度 280 到 310°C

料筒中部温度 280 到 310°C

料筒前部温度 280 到 310°C

射嘴温度 280 到 310°C

加工（熔体）温度 285 到 305°C

模具温度 65.0 到 95.0°C

 

 

 

 

 

东莞市双帮塑胶原料有限公司大量销售塑料聚酰胺66  Ascend Performance Materials Operations LLC 尼龙66  美国首诺    尼龙66 Vydyne® R530H NAT为塑料价格行情每天都有新的变化前天的报价不等于今天的报价。如果需要新的价格请电：13549213581，肖生。